6061 aluminum plate has high strength, good corrosion resistance and oxidation resistance. It is widely used in automatic mechanical parts, precision machining, automobile chassis, cake mold, etc. It is well received by users, but 6061 aluminum plate T6, F, O three What are the differences between the states and the advantages of car chassis and cake molds? Now there are Henan aluminum plate manufacturers to explain in detail for you.

6061 aluminum sheet (1)
6061 aluminum sheet (1)

6061 aluminum plate T6, F, O three states difference

The 6061 aluminum sheet has been widely used after heat treatment. The 6061 aluminum alloy thick plate is used in automated mechanical parts, precision machining, and various mold manufacturing.

6061 aluminum sheet (2)
6061 aluminum sheet (2)

6061 aluminum plate common state:

The T6 state is the most used of aluminum alloy 6061. The 6061 aluminum plate is in this state by quenching-slicing-stretching machine-aging treatment-saw-polish-packaging. The whole production cycle is about 10 days. After the solution heat treatment, it does not need to be cold-worked, and can be straightened and leveled without affecting the mechanical properties.

The F state is 6061 aluminum alloy free processing state, suitable for special products for work hardening and heat treatment conditions during the molding process. F-state production cycle is very short: plate cutting – sawing – polishing (also can not be polished, according to customer requirements) – packaging, the entire process is arranged smoothly for 3 days to ship, F-state mechanical properties do not make specifications, customers can according to their own needs The F state is further subjected to heat treatment processing and used in a desired state. The corresponding price is also the cheapest.

The O state is a 6061 aluminum plate that has been fully annealed to obtain the lowest strength processed product. Applicable to 6061 aluminum sheet 8.0 or less, the production process: cold rolled finished product thickness – stretch bending cleaning – complete annealing – flying shearing (or bending and bending finished products) – packaging and storage, etc. The cycle is second only to the T6 state.